Silicone hydrophobic powder weathering test
Silicone hydrophobic powder is a crucial dry-mix mortar additive based on silicone compounds. After application, it imparts a lotus-leaf effect to the surface layer, preventing water ingress while offering excellent water resistance, breathability, and durability.
This test involved preparing a dry-mix mortar containing silicone hydrophobic powder and an organic polymer redispersible polymer powder (RDP). After mixing with water, test specimens measuring 160*40*40 mm were formed, placed outdoors for curing, and observed.
-
Specimen Casting Date: August 27, 2025
-
Outdoor Curing Period: 4 Months
-
Observation Date: December 27, 2025
Observation & Conclusion:
After 4 months of outdoor exposure, observation indicates that while the surface lotus-leaf (hydrophobic) effect has diminished, the hydrophobic effect within the internal structure of the specimen remains distinctly evident.
SIDLEYCHEM Product Recommendations:
Drymix mortar Tech+
Why Does Tile Adhesive Lose Bond Strength After Water Immersion?
Tile adhesive loses bond strength after water immersion? Learn how RDP, water ratio, curing, and polymer balance affect wet adhesion… Continue reading
Waterproof Mortar Still Absorbs Water: Causes & Fixes
Waterproof mortar still absorbs water? Learn how hydrophobic powder, porosity, water ratio, and curing affect water resistance… Continue reading
Self-Leveling Mortar Flow Loss: Causes & Solutions
Self-leveling mortar may have good initial flow but lose workability within minutes. Learn how PCE, cellulose ether, setting time, and temperature affect flow retention… Continue reading
Tile Adhesive Slipping After Adding HPMC: Causes & Fixes
Tile adhesive can still slip even after increasing HPMC. Learn how HPMC grade, water demand, starch ether, thixotropy, and formulation balance affect slip resistance… Continue reading
Pinholes in Self-Leveling Mortar: Defoamer, Mixing, or Substrate?
Pinholes in self-leveling mortar are not always caused by insufficient defoamer. This guide explains how to distinguish formulation foam, mixing-induced air, substrate outgassing, and insufficient healing time through a simple three-surface comparison test and practical corrective actions… Continue reading
Why Does Dry Mortar Have Poor Water Retention?
Learn why dry mortar has poor water retention and how HPMC and MHEC can improve water retention, workability, and cement hydration in dry-mix mortar… Continue reading
Dry-Mix Mortar Summer Formulation Adjustment
Why does the same formulation fail in summer? The key is cellulose ether. High temperatures cause ordinary HPMC water retention to drop sharply — increase dosage by 0.1%-0.2%, switch to high gel temperature grades, and combine with retarders. This article gives three practical adjustment directions to tackle summer construction challenges… Continue reading
Mortar Setting Too Fast in Summer Heat?
Mortar drying out in half an hour on summer job sites? High-temperature accelerated hydration is the culprit. This article breaks down the features and selection of sodium gluconate, citric acid, tartaric acid, and boric acid retarders, with dosage adjustment and blending strategies to tackle summer construction challenges… Continue reading
Why Does Dry Mix Mortar Cake During Storage?
Discover why dry mix mortar cakes during storage and transportation. Learn how moisture, packaging, raw materials, and formulation affect storage stability, and explore practical solutions to maintain product quality… Continue reading
Why Does Tile Grout Change Color After Curing?
Discover the most common causes of tile grout color inconsistency after curing and learn practical solutions through proper formulation, pigment selection, moisture control, and construction practices… Continue reading